Fluoroethylenepropylene Ferroelectret Films with Cross-tunnel Structure for Piezoelectric Transducers and Micro Energy Harvesters

2015-07-09 浏览:

Abstract

Layered fluoroethylenepropylene (FEP) ferroelectret films with cross-tunnel structure were fabricated from sheets of FEP films by template-patterning followed by a fusion-bonding process and contact charging. The typical piezoelectric d33 coefficients, measured by a quasi-static method of samples not annealed, are in the range of 1000-3700 pC/N. The resonance behavior of the samples is analyzed by dielectric spectroscopy which also yields Young’s modulus. Microphones built with such films exhibit a somewhat decreasing frequency response up to 1 kHz, an increase of the responses due to diffraction effects at higher frequencies, and eventually a peak probably due to a thickness resonance at about 40 kHz. Annealing at 125 °C indicates that the sensitivity stabilizes at about 40 percent of the original value. From this data, stable dynamic d33 coefficients of up to 300 pC/N can be calculated. A micro energy harvesting generator utilizing these films and based on the excitation of thickness vibrations is also described. With an active area of 4.3 cm2 and a seismic mass of 69.5 g, power up to 0.5 μW referred to an acceleration of 1g can be generated at a frequency of 120 Hz.


by Xiaoqing Zhang,   Gerhard M. Sessler, and Yujie Wang


Journal of Applied Physics  116, (2014)074109 

关于我们 | 产品展示 | 公司动态 | 人才招聘 | 联系方式
版权所有:上海驻极新材料科技有限公司 官网网站:www.electretsh.cn
技术支持:默默网络 沪ICP备15022627号-1